Kanthal® is a world-leading brand for products and services in the area of industrial heating technology and resistance materials.
We are an Authorized Distributors & Represent Kanthal® from last 2 Decades.
Product Details:
| Minimum Order Quantity | 1 Kg |
| Usage/Application | Industrial |
| Thickness | 10 mm - 1.02 mm |
| Highest Temperature | Up to 1500 Degree C |
| Brand | Kanthal Sweden |
| Hardness | 230 HV |
| Color | Golden & Blue Annealed |
| Melting Point | Up to 1500 Degree C |
| Certification | Kanthal Authorized Certificate |
Kanthal APM is an advanced powder-metallurgical, dispersion-strengthened, ferritic iron-chromium-aluminium alloy (FeCrAl alloy) for use at temperatures up to 1425°C (2600°F). The alloy is characterized by exceptionally good form stability and oxidation resistance.
Kanthal APM has low tendency to ageing and low resistance change. It has excellent surface oxide properties, which gives good protection in corrosive atmospheres as well as in atmospheres with high carbon potential, and no scaling.
The unique combination of excellent oxidation properties and form stability contributes to long element service life. The alloy''s superior form stability reduces the amount of element support.
Typical applications for Kanthal APM are in high-temperature furnaces for firing of ceramics, heat treatment, in laboratory furnaces, in furnaces for electronic industries and in diffusion furnaces.
| C % | Si % | Mn % | Cr % | Al % | Fe % | |
|---|---|---|---|---|---|---|
| †Nominal composition | 5.8 | Bal. | ||||
| Min | - | - | - | 20.5 | - | |
| Max | 0.08 | 0.7 | 0.4 | 23.5 | - |
| Wire size | Yield strength | Tensile strength | Elongation | Hardness |
|---|---|---|---|---|
| Ø | Rp0.2 | Rm | A | |
| mm | MPa | MPa | % | Hv |
| 4.0 | 470 | 680 | 20 | 230 |
| Temperature °C | 900 | 1000 | 1100 | 1200 | 1300 |
|---|---|---|---|---|---|
| MPa | 40 | 23 | 16 | 12 | 9 |
Ultimate tensile strength - deformation rate 6.2 x 10-2/min
CREEP STRENGTH - 1% ELONGATION IN 1000 H| Temperature °C | 800 | 900 |
|---|---|---|
| MPa | 8.2 | 3.5 |
| Temperature °C | 1100 | 1200 | 1300 | 1400 |
|---|---|---|---|---|
| MPa | 2.3 | 1.2 | 0.7 | 0.4 |
| Time | 800°C | 1472°F | 1000°C | 1832°F | 1200°C | 2192°F | 1400°C | 2552°F |
|---|---|---|---|---|---|---|---|---|
| h | MPa | psi | MPa | psi | MPa | psi | MPa | psi |
| 100 | 15.0 | 2176 | 5.6 | 812 | 3.3 | 478 | 1.3 | 189 |
| 1000 | 11.3 | 1640 | 3.4 | 478 | 1.6 | 232 | 0.5 | 72 |
| 10000 | 8.2 | 1190 | 2.2 | 320 | 0.7 | 100 | 0.2 | 30 |
The data in the tables apply to material with fine grain structure in the temperature range from 800°C to 900°C,
and to material with coarse grain structure in the temperature range from 1100°C to 1400°C.
In the delivery state KANTHAL APM always has a fine grain structure. After use for a certain period of time , the grain size becomes coarse.
Additional Information:
Product Details:
| Minimum Order Quantity | 1 Kg |
| Size/Dimension | Width: 40 mm to 5 mm, Thickness: 4 mm to 0.1 mm |
| Material | FeCrAl |
| Operating Temperature | Up to 1400 Degree C |
| Certification | Kanthal Authorized Certificate |
| Brand | Kanthal (Sweden) |
| Melting Point | Up to 1500 Degree C |
Kanthal A-1 is a ferritic iron-chromium-aluminium alloy (FeCrAl alloy) for use at temperatures up to 1400°C (2550°F). The alloy is characterized by high resistivity and very good oxidation resistance.
Typical applications for Kanthal A-1 are electrical heating elements in high-temperature furnaces for heat treatment, ceramics, glass, steel, and electronics industries.
Chemical composition
|
C % |
Si % |
Mn % |
Cr % |
Al % |
Fe % |
|
|
Nominal composition |
5.8 |
Bal. |
||||
|
Min |
- |
- |
- |
20.5 |
- |
|
|
Max |
0.08 |
0.7 |
0.4 |
23.5 |
- |
|
Mechanical properties
|
Wire size |
Yield strength |
Tensile strength |
Elongation |
Hardness |
|
Ø |
Rp0.2 |
Rm |
A |
|
|
mm (in) |
MPa (ksi) |
MPa (ksi) |
% |
Hv |
|
1.0 (0.04) |
545 (79) |
760 (110) |
20 |
240 |
|
4.0 (0.16) |
475 (69) |
680 (99) |
18 |
230 |
|
MECHANICAL PROPERTIES AT ELEVATED TEMPERATURE |
|||||
|
Temperature °C |
900 |
1000 |
1100 |
1200 |
1300 |
|
Temperature °F |
1652 |
1832 |
2012 |
2192 |
2372 |
|
MPa |
34 |
18 |
10 |
6 |
4 |
|
ksi |
4.9 |
2.6 |
1.5 |
0.9 |
0.6 |
Additional Information:
Product Details:
| Minimum Order Quantity | 1 Kg |
| Material | Heating Wire |
| Usage/Application | Industrial & Appliance |
| Thickness | 10 mm - 1.02 mm |
| Highest Temperature | Up to 1300 Degree C |
| Brand | Kanthal (Sweden) |
| Shape | Round |
| Color | Golden & Bright Annealed |
| Melting Point | Up to 1500 Degree C |
| Hardness | 230 Hv |
| Certification | Kanthal Authorized Certificate |
Kanthal D is a ferritic iron-chromium-aluminium alloy (FeCrAl alloy) for use at temperatures up to 1300°C (2370°F). The alloy is characterized by high resistivity and good oxidation resistance.
Kanthal® D is used in home appliances and industrial furnaces. Typical applications in home appliances include metal sheathed tubular elements for dishwashers, elements embedded in ceramics for panel heaters, cartridge elements in metal dies, heating cables and rope heaters in defrosting and deicing elements, mica elements used in irons, quartz tube heaters for space heating, industrial infrared dryers, in coils on molded ceramic fibre for boiling plates with ceramic hobs, in bead insulated coils for panel heaters, in suspended coil elements for air heaters in laundry dryers.
In industrial applications Kanthal D is used in, for example, terminals to furnace elements, porcupine elements for air heating, and in furnace heating elements.
C % | Si % | Mn % | Cr % | Al % | Fe % | |
Nominal composition | 4.8 | Bal. | ||||
Min | - | - | - | 20.5 | - | |
Max | 0.08 | 0.7 | 0.5 | 23.5 | - |
Wire size | Yield strength | Tensile strength | Elongation | Hardness |
Ø | Rp0.2 | Rm | A | |
mm (in) | MPa (ksi) | MPa (ksi) | % | Hv |
1.0 (0.04) | 485 (70) | 670 (97) | 23 | 230 |
4.0 (0.16) | 450 (65) | 650 (94) | 18 | 230 |
MECHANICAL PROPERTIES AT ELEVATED TEMPERATURE | |
Temperature °C (°F) | 900 (1652) |
MPa (ksi) | 34 (4.9) |
Ultimate tensile strength - deformation rate 6.2 x 10-2/min
CREEP STRENGTH - 1% ELONGATION IN 1000 H | ||
Temperature °C (°F) | 800 (1472) | 900 (1652) |
MPa (psi) | 1.2 (170) | 0.5 (73) |
Additional Information:
Product Details:
| Minimum Order Quantity | 1 Kg |
| Usage/Application | Industrial |
| Thickness | 10 mm - 1.02 mm |
| Brand | Kanthal (Sweden) |
| Hardness | 230 HV |
| Highest Temperature | Up to 1500 Degree C |
| Color | Golden & Blue Annealed |
| Certification | Kanthal Authorized Certificate |
| Melting Point | Up to 1500 Degree C |
Kanthal A-1 is a ferritic iron-chromium-aluminium alloy (FeCrAl alloy) for use at temperatures up to 1400°C (2550°F). The alloy is characterized by high resistivity and very good oxidation resistance.
Typical applications for Kanthal A-1 are electrical heating elements in high-temperature furnaces for heat treatment, ceramics, glass, steel, and electronics industries.
Chemical composition
|
C % |
Si % |
Mn % |
Cr % |
Al % |
Fe % |
|
|
Nominal composition |
5.8 |
Bal. |
||||
|
Min |
- |
- |
- |
20.5 |
- |
|
|
Max |
0.08 |
0.7 |
0.4 |
23.5 |
- |
|
Mechanical properties
|
Wire size |
Yield strength |
Tensile strength |
Elongation |
Hardness |
|
Ø |
Rp0.2 |
Rm |
A |
|
|
mm (in) |
MPa (ksi) |
MPa (ksi) |
% |
Hv |
|
1.0 (0.04) |
545 (79) |
760 (110) |
20 |
240 |
|
4.0 (0.16) |
475 (69) |
680 (99) |
18 |
230 |
|
MECHANICAL PROPERTIES AT ELEVATED TEMPERATURE |
|||||
|
Temperature °C |
900 |
1000 |
1100 |
1200 |
1300 |
|
Temperature °F |
1652 |
1832 |
2012 |
2192 |
2372 |
|
MPa |
34 |
18 |
10 |
6 |
4 |
|
ksi |
4.9 |
2.6 |
1.5 |
0.9 |
0.6 |
Additional Information:
Product Details:
| Minimum Order Quantity | 1 Kg |
| Size/Dimension | Width: 40 mm to 5 mm,Thickness: 4 mm to 0.1 mm |
| Material | FeCrAl |
| Usage | Furnace Heating Element |
| Operating Temperature | Up to 1400 Degree C |
| Origin | Sweden |
| Certification | Kanthal Authorized Certificate |
| Brand | Kanthal Sweden |
| Melting Point | Up to 1500 Degree C |
Kanthal APM is an advanced powder-metallurgical, dispersion-strengthened, ferritic iron-chromium-aluminium alloy (FeCrAl alloy) for use at temperatures up to 1425°C (2600°F). The alloy is characterized by exceptionally good form stability and oxidation resistance.
Kanthal APM has low tendency to ageing and low resistance change. It has excellent surface oxide properties, which gives good protection in corrosive atmospheres as well as in atmospheres with high carbon potential, and no scaling.
The unique combination of excellent oxidation properties and form stability contributes to long element service life. The alloy''''''''s superior form stability reduces the amount of element support.
Typical applications for Kanthal APM are in high-temperature furnaces for firing of ceramics, heat treatment, in laboratory furnaces, in furnaces for electronic industries and in diffusion furnaces.
Chemical composition
| C % | Si % | Mn % | Cr % | Al % | Fe % | |
|---|---|---|---|---|---|---|
| †Nominal composition | 5.8 | Bal. | ||||
| Min | - | - | - | 20.5 | - | |
| Max | 0.08 | 0.7 | 0.4 | 23.5 | - |
Mechanical properties
| Wire size | Yield strength | Tensile strength | Elongation | Hardness |
|---|---|---|---|---|
| Ø | Rp0.2 | Rm | A | |
| mm | MPa | MPa | % | Hv |
| 4.0 | 470 | 680 | 20 | 230 |
MECHANICAL PROPERTIES AT ELEVATED TEMPERATURE
| Temperature °C | 900 | 1000 | 1100 | 1200 | 1300 |
|---|---|---|---|---|---|
| MPa | 40 | 23 | 16 | 12 | 9 |
Ultimate tensile strength - deformation rate 6.2 x 10-2/min
CREEP STRENGTH - 1% ELONGATION IN 1000 H| Temperature °C | 800 | 900 |
|---|---|---|
| MPa | 8.2 | 3.5 |
CREEP STRENGTH - 0.1% ELONGATION IN 1000 H
| Temperature °C | 1100 | 1200 | 1300 | 1400 |
|---|---|---|---|---|
| MPa | 2.3 | 1.2 | 0.7 | 0.4 |
| Time | 800°C | 1472°F | 1000°C | 1832°F | 1200°C | 2192°F | 1400°C | 2552°F |
|---|---|---|---|---|---|---|---|---|
| h | MPa | psi | MPa | psi | MPa | psi | MPa | psi |
| 100 | 15.0 | 2176 | 5.6 | 812 | 3.3 | 478 | 1.3 | 189 |
| 1000 | 11.3 | 1640 | 3.4 | 478 | 1.6 | 232 | 0.5 | 72 |
| 10000 | 8.2 | 1190 | 2.2 | 320 | 0.7 | 100 | 0.2 | 30 |
The data in the tables apply to material with fine grain structure in the temperature range from 800°C to 900°C,
and to material with coarse grain structure in the temperature range from 1100°C to 1400°C.
In the delivery state KANTHAL APM always has a fine grain structure. After use for a certain period of time , the grain size becomes coarse.
Additional Information:
Product Details:
| Minimum Order Quantity | 1 Kg |
| Usage/Application | Furnace Heating Element |
| Thickness | 40 mm, 39 mm, 30 mm, 20 mm, 18 mm, 16 mm, 14 mm, 12 mm, 10 mm, 8.00 mm, 6.00 mm |
| Brand | Kanthal (Sweden) |
| Shape | Round |
| Length | 2000 mm, 2250 mm, 4000 mm & Customized |
| Hardness | 230 HV |
| Highest Temperature | Up to 1425 Degree C |
| Melting Point | 1500 Degree Celsius |
| Origin | Sweden |
| Certification | Kanthal Authorized Certificate |
| Color | Bright Annealed |
Kanthal APM is an advanced powder-metallurgical, dispersion-strengthened, ferritic iron-chromium-aluminium alloy (FeCrAl alloy) for use at temperatures up to 1425°C (2600°F). The alloy is characterized by exceptionally good form stability and oxidation resistance.
Kanthal APM has low tendency to ageing and low resistance change. It has excellent surface oxide properties, which gives good protection in corrosive atmospheres as well as in atmospheres with high carbon potential, and no scaling.
The unique combination of excellent oxidation properties and form stability contributes to long element service life. The alloy''s superior form stability reduces the amount of element support.
Typical applications for Kanthal APM are in high-temperature furnaces for firing of ceramics, heat treatment, in laboratory furnaces, in furnaces for electronic industries and in diffusion furnaces.
| C % | Si % | Mn % | Cr % | Al % | Fe % | |
|---|---|---|---|---|---|---|
| †Nominal composition | 5.8 | Bal. | ||||
| Min | - | - | - | 20.5 | - | |
| Max | 0.08 | 0.7 | 0.4 | 23.5 | - |
| Wire size | Yield strength | Tensile strength | Elongation | Hardness |
|---|---|---|---|---|
| Ø | Rp0.2 | Rm | A | |
| mm | MPa | MPa | % | Hv |
| 4.0 | 470 | 680 | 20 | 230 |
| Temperature °C | 900 | 1000 | 1100 | 1200 | 1300 |
|---|---|---|---|---|---|
| MPa | 40 | 23 | 16 | 12 | 9 |
Ultimate tensile strength - deformation rate 6.2 x 10-2/min
CREEP STRENGTH - 1% ELONGATION IN 1000 H| Temperature °C | 800 | 900 |
|---|---|---|
| MPa | 8.2 | 3.5 |
| Temperature °C | 1100 | 1200 | 1300 | 1400 |
|---|---|---|---|---|
| MPa | 2.3 | 1.2 | 0.7 | 0.4 |
| Time | 800°C | 1472°F | 1000°C | 1832°F | 1200°C | 2192°F | 1400°C | 2552°F |
|---|---|---|---|---|---|---|---|---|
| h | MPa | psi | MPa | psi | MPa | psi | MPa | psi |
| 100 | 15.0 | 2176 | 5.6 | 812 | 3.3 | 478 | 1.3 | 189 |
| 1000 | 11.3 | 1640 | 3.4 | 478 | 1.6 | 232 | 0.5 | 72 |
| 10000 | 8.2 | 1190 | 2.2 | 320 | 0.7 | 100 | 0.2 | 30 |
The data in the tables apply to material with fine grain structure in the temperature range from 800°C to 900°C,
and to material with coarse grain structure in the temperature range from 1100°C to 1400°C.
In the delivery state KANTHAL APM always has a fine grain structure. After use for a certain period of time , the grain size becomes coarse.
Additional Information:
Product Details:
| Minimum Order Quantity | 1 Kg |
| Heater Type | Furnace |
| Material | Stainless Steel |
| Usage/Application | Furnace Heating Elements |
| Thickness | 40 mm, 39 mm, 30 mm, 20 mm, 18 mm, 16 mm, 14 mm, 12 mm, 10 mm, 8.00 mm, 6.00 mm |
| Brand | Kanthal (Sweden) |
| Shape | Round |
| Length | 2000 mm, 2250 mm, 4000 mm |
| Temperature | Up to 1350 Degree Celsius |
| Hardness | 230 HV |
| Material Grade | FeCrAl |
| Highest Temperature | Up to 1300 Degree C |
| Origin | Sweden |
| Certification | Kanthal Authorized Certificate |
Kanthal D is a ferritic iron-chromium-aluminium alloy (FeCrAl alloy) for use at temperatures up to 1300°C (2370°F). The alloy is characterized by high resistivity and good oxidation resistance.
Kanthal® D is used in home appliances and industrial furnaces. Typical applications in home appliances include metal sheathed tubular elements for dishwashers, elements embedded in ceramics for panel heaters, cartridge elements in metal dies, heating cables and rope heaters in defrosting and deicing elements, mica elements used in irons, quartz tube heaters for space heating, industrial infrared dryers, in coils on molded ceramic fibre for boiling plates with ceramic hobs, in bead insulated coils for panel heaters, in suspended coil elements for air heaters in laundry dryers.
In industrial applications Kanthal D is used in, for example, terminals to furnace elements, porcupine elements for air heating, and in furnace heating elements.
|
C % |
Si % |
Mn % |
Cr % |
Al % |
Fe % |
|
|
Nominal composition |
4.8 |
Bal. |
||||
|
Min |
- |
- |
- |
20.5 |
- |
|
|
Max |
0.08 |
0.7 |
0.5 |
23.5 |
- |
|
Wire size |
Yield strength |
Tensile strength |
Elongation |
Hardness |
|
Ø |
Rp0.2 |
Rm |
A |
|
|
mm (in) |
MPa (ksi) |
MPa (ksi) |
% |
Hv |
|
1.0 (0.04) |
485 (70) |
670 (97) |
23 |
230 |
|
4.0 (0.16) |
450 (65) |
650 (94) |
18 |
230 |
|
MECHANICAL PROPERTIES AT ELEVATED TEMPERATURE |
|
|
Temperature °C (°F) |
900 (1652) |
|
MPa (ksi) |
34 (4.9) |
Ultimate tensile strength - deformation rate 6.2 x 10-2/min
|
CREEP STRENGTH - 1% ELONGATION IN 1000 H |
||
|
Temperature °C (°F) |
800 (1472) |
900 (1652) |
|
MPa (psi) |
1.2 (170) |
0.5 (73) |
Additional Information:
Product Details:
| Minimum Order Quantity | 1 Kg |
| Color | Bright Annealed |
| Melting Point | 1050 Degree Celsius |
| Density | 7.80 g/cm3 |
| Magnetic properties | The material is non-magnetic |
| Certification | Kanthal Authorized Certificate |
| Usage/Application | Industrial |
| Brand | Kanthal (Sweden) |
Nikrothal® 30 is an austenitic nickel-chromium alloy (NiCr alloy) for use at temperatures up to 1050°C (1920°F). The alloy is characterized by high resistivity and good oxidation resistance. It has good ductility after use and excellent weldability.
Typical applications for Nikrothal® 30 are solid hot plates, open coil heaters in HVAC systems, night-storage heaters, convection heaters, heavy duty rheostats and fan heaters. Nikrothal® 30 is also used for heating cables and rope heaters in defrosting and de-icing elements, electric blankets and pads, car seats, baseboard heaters, floor heaters and resistors.
|
|
Si % |
Mn % |
Cr % |
Ni % |
Fe % |
Trace Elements |
|
|
Nominal composition |
Bal. |
Added |
|||||
|
Min |
1.6 |
20.0 |
30.0 |
||||
|
Max |
0.15 |
2.5 |
1.0 |
22.0 |
33.0 |
Additional Information: